XL128 high reinforcing, high abrasion white carbon black
   Project
   Technical Index
   Testing Method
   Whiteness
   Superior or equivalent
to master standard
   HG/T3063-1999(eqv ISO 5794-1:1994)
   Silica content(dry)%
   ≥90
   HG/T3062-1999(eqv ISO 5794-1:1994)
   Heating loss % 105℃ 2h
   4.0-7.0
   HG/T3065-1999(eqv ISO 5794-1:1994)
   Ignition loss(dry)% 1000℃ 2h
   3.0-6.0
   HG/T3066-1999(eqv ISO 5794-1:1994)
   PH value
   6.0-7.5
   HG/T3067-1999(eqv ISO 5794-1:1994)
   BET specific surface area m²/g
   146-168
   HG/T3073-1999(eqv ISO 4652-1:1994)
   DBP absorbing oil cm³/g
   2.0-3.0
   HG/T3072-1999(eqv ISO 5794-1:1994)
   Total iron content mg/kg
   <500
   HG/T3070-1999(eqv ISO 5794-1:1994)
   Standard recipe sizing material performance(150×10
   ISO5794/2
   500% tensile stress
   5.5-8.0
   HG/T 2404-1992
   Breaking strength  Mpa
   ≥17.0
   HG/T 2404-1992
   Tensile elongation%
   ≥675
   HG/T 2404-1992
   Application
   mainly applied to tire, as well as semitransparent color rubber sole, medicine carrier, and feed additive.
   Note
   Adjust product mesh numbers according to the user requirement.
XL228 high reinforcing, high abrasion white carbon black
   Project
   Technical Index
   Testing Method
   Whiteness
   Superior or equivalent to master standard
   HG/T3063-1999(eqv ISO 5794-1:1994)
   Silica content(dry)%
   ≥90
   HG/T3062-1999(eqv ISO 5794-1:1994)
   Heating loss % 105℃ 2h
   4.0-7.0
   HG/T3065-1999(eqv ISO 5794-1:1994)
   Ignition loss(dry)% 1000℃ 2h
   3.0-6.0
   HG/T3066-1999(eqv ISO 5794-1:1994)
   PH value
   5.5-7.0
   HG/T3067-1999(eqv ISO 5794-1:1994)
   BET specific surface area m²/g
   168-188
   HG/T3073-1999(eqv ISO 4652-1:1994)
   DBP absorbing oil cm³/g
   2.0-3.0
   HG/T3072-1999(eqv ISO 5794-1:1994)
   Total iron content mg/kg
   <500
   HG/T3070-1999(eqv ISO 5794-1:1994)
   Total copper content mg/kg
   <30
   HG/T3068-1999(eqv ISO 5794-1:1994)
   Total manganese content mg/kg
   <50
   HG/T3069-1999(eqv ISO 5794-1:1994)
   Standard recipe sizing material performance(150×15
   ISO5794/2
   500% tensile stress at a given elongation
   5.5-8.0
   HG/T 2404-1992
   Breaking strength  Mpa
   ≥17.0
   HG/T 2404-1992
   Elongation at failure%
   ≥700
   HG/T 2404-1992
   Application
   mainly applied to radial tire, as well as sole, rubber tubes, rubber belt, solid tire, cycle tire colored tore, feed additive, medicine carrier and so on.
   Note
   Adjust product mesh numbers according to the user requirement.
XL328 high transparent, high reinforcing, high abrasion white carbon black
   Project
   Technical Index
   Testing Method
   Whiteness
   Superior or equivalent to master standard
   HG/T3063-1999(eqv ISO 5794-1:1994)
   Silica content(dry)%
   ≥90
   HG/T3062-1999(eqv ISO 5794-1:1994)
   Heating loss % 105℃ 2h
   4.0-8.0
   HG/T3065-1999(eqv ISO 5794-1:1994)
   Ignition loss(dry) % 1000℃ 2h
   3.0-6.0
   HG/T3066-1999(eqv ISO 5794-1:1994)
   PH value
   6.5-7.0
   HG/T3067-1999(eqv ISO 5794-1:1994)
   BET specific surface area m²/g
   200-260
   HG/T3073-1999(eqv ISO 4652-1:1994)
   DBP absorbing oil cm³/g
   3.0-3.6
   HG/T3072-1999(eqv ISO 5794-1:1994)
   Total iron content mg/kg
   <500
   HG/T3070-1999(eqv ISO 5794-1:1994)
   Application
   mainly applied to medicine, food, powder extinguishing agent, paint, dope, high transparent rubber .sole and so on.
White carbon black
White carbon black
White carbon black
Workshop
Previous:Have no
Next:silica
Copyright(C)2012-2013 Shandong Xiangli Silicon Industry Co., Ltd.
Address:Wang Mugong Economic Development Zone, Qingzhou City, Shandong Province Ltd Support:qzshangwu